BO-LITE 9 x
8
BO-LITE are mesh fabrics comprised of 22% high tenacity
polyester yarn and 78% flexible foamed PVC. The yarns are
intimately bonded at the crossover points and the degree
of openness is dependent on the fabric construction.
BO-LITE 9 x 8 is suitable for many decorative and industrial
applications. It is widely used for premium quality tennis
court windscreen. It is also used for horticultural shading
in greenhouses and outside areas, personnel sunscreen, and
in the fabrication of outdoor stage sets. It offers superior
longevity and aesthetics compared with conventional olefinic
shade fabrics.
TYPICAL USES
Bo-Lite fabric is excellent for:
Construction Debris Liner
Patio Umbrellas
Sun Shade
Hot Tub Covers
AVAILABLE SIZES
9 x 8
10 x 9
11 x 10
4 x 5
7 x 5
|
|
| Characteristics |
9
x 8 |
|
| Construction: |
9
x 8 ends/inch |
|
| Coating: |
Flexible
Foamed PVC |
|
| Core
Yarn: |
1000
denier Polyester |
|
| Fabric
Weight: |
9
- 10 oz/ sq yd |
|
| Tensile
Strength: |
(ASTM
D-1682) - Warp: 170 lbs/inch minimum
Grab - Fill: 155 lbs/inch minimum |
|
| Tear
Strength: |
(ASTM
D-2261) - 58 lbs minimum warp
Tongue-single rip - 55 lbs minimum fill |
|
| Mullen
Burst Strength: |
(ASTM
D-3786) - 265 lbs/sq in |
|
| Caliper: |
(Fabric
thickness) - 45-50 mils |
|
| Fire
Retardancy: |
As
required. Mill run fabric is self-
extinguishing in horizontal burning
mode. Increased fire retardancy
can be supplied upon special order
to meet specified tests. |
|
| Cold
Crack: |
No
cracking after 24 hours @ -40 degrees F, 2" mandrel |
|
| Fabric
Stretch: |
Warp
4% maximum
(ASTM D1682, 27 lbs/inch) - Fill 4% maximum |
|
| UV
Resistance: |
(ASTM
G53) - 1000 hours
QUV exposure - slight color deterioration |
|
| Shade
Factor: |
80%
(78-82%) |
| |
|